PC 基础创新塑料(南沙) LUX2114物性信息：
|
物理性能
|
额定值
|
单位制
|
测试方法
|
|
比重
|
|
|
ASTM D792
|
|
--
|
1.20
|
g/cm3
|
ASTM D792
|
|
--
|
1.19
|
g/cm3
|
ASTM D792
|
|
特定体积
|
0.830
|
cm3/g
|
ASTM D792
|
|
熔流率（熔体流动速率） (300°C/1.2 kg)
|
18
|
g/10 min
|
ASTM D1238
|
|
收缩率 - 流动 (3.20 mm)
|
0.50 到 0.70
|
%
|
内部方法
|
|
吸水率
|
|
|
ASTM D570
|
|
24 hr
|
0.15
|
%
|
ASTM D570
|
|
平衡, 23°C
|
0.35
|
%
|
ASTM D570
|
|
平衡, 100°C
|
0.58
|
%
|
ASTM D570
|
|
室外适用性
|
f2
|
|
UL 746C
|
|
硬度
|
额定值
|
单位制
|
测试方法
|
|
洛氏硬度
|
|
|
ASTM D785
|
|
M 级
|
70
|
|
ASTM D785
|
|
R 级
|
118
|
|
ASTM D785
|
|
机械性能
|
额定值
|
单位制
|
测试方法
|
|
抗张强度 1
|
|
|
ASTM D638
|
|
屈服
|
62.1
|
MPa
|
ASTM D638
|
|
断裂
|
65.5
|
MPa
|
ASTM D638
|
|
伸长率 2
|
|
|
ASTM D638
|
|
屈服
|
7.0
|
%
|
ASTM D638
|
|
断裂
|
110
|
%
|
ASTM D638
|
|
弯曲模量 3(50.0 mm 跨距)
|
2340
|
MPa
|
ASTM D790
|
|
弯曲强度 4(屈服, 50.0 mm 跨距)
|
93.1
|
MPa
|
ASTM D790
|
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮)
|
10.0
|
mg
|
ASTM D1044
|
|
冲击性能
|
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度 5
|
|
|
ISO 179/1eA
|
|
-30°C
|
12
|
kJ/m2
|
ISO 179/1eA
|
|
23°C
|
65
|
kJ/m2
|
ISO 179/1eA
|
|
简支梁无缺口冲击强度 6
|
|
|
ISO 179/1eU
|
|
-30°C
|
无断裂
|
|
ISO 179/1eU
|
|
23°C
|
无断裂
|
|
ISO 179/1eU
|
|
悬壁梁缺口冲击强度
|
|
|
|
|
23°C
|
600
|
J/m
|
ASTM D256
|
|
-30°C 7
|
11
|
kJ/m2
|
ISO 180/1A
|
|
23°C 8
|
65
|
kJ/m2
|
ISO 180/1A
|
|
无缺口悬臂梁冲击
|
|
|
|
|
23°C
|
3200
|
J/m
|
ASTM D4812
|
|
-30°C 9
|
无断裂
|
|
ISO 180/1U
|
|
23°C 10
|
无断裂
|
|
ISO 180/1U
|
|
落锤冲击 (23°C)
|
169
|
J
|
ASTM D3029
|
|
拉伸冲击强度 11
|
546
|
kJ/m2
|
ASTM D1822
|
|
热性能
|
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|
|
ASTM D648
|
|
0.45 MPa, 未退火, 6.40 mm
|
138
|
°C
|
ASTM D648
|
|
1.8 MPa, 未退火, 6.40 mm
|
132
|
°C
|
ASTM D648
|
|
维卡软化温度
|
154
|
°C
|
ASTM D1525 12
|
|
Ball Pressure Test (125°C)
|
Pass
|
|
IEC 60695-10-2
|
|
线形热膨胀系数 - 流动 (-40 到 95°C)
|
6.8E-5
|
cm/cm/°C
|
ASTM E831
|
|
比热
|
1260
|
J/kg/°C
|
ASTM C351
|
|
导热系数
|
0.25
|
W/m/K
|
ASTM C177
|
|
RTI Elec
|
80.0
|
°C
|
UL 746
|
|
RTI Imp
|
80.0
|
°C
|
UL 746
|
|
RTI
|
80.0
|
°C
|
UL 746
|
|
电气性能
|
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
> 1.0E+17
|
ohms·cm
|
ASTM D257
|
|
介电强度 (3.20 mm, in Air)
|
15
|
kV/mm
|
ASTM D149
|
|
介电常数
|
|
|
ASTM D150
|
|
50 Hz
|
3.17
|
|
ASTM D150
|
|
60 Hz
|
3.17
|
|
ASTM D150
|
|
1 MHz
|
2.96
|
|
ASTM D150
|
|
耗散因数
|
|
|
ASTM D150
|
|
50 Hz
|
9.0E-4
|
|
ASTM D150
|
|
60 Hz
|
9.0E-4
|
|
ASTM D150
|
|
1 MHz
|
0.010
|
|
ASTM D150
|
|
|
|
|
|
可燃性
|
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (0.750 到 1.65 mm)
|
V-2
|
|
UL 94
|
|
灼热丝易燃指数
|
|
|
IEC 60695-2-12
|
|
0.750 mm
|
750
|
°C
|
IEC 60695-2-12
|
|
1.50 mm
|
850
|
°C
|
IEC 60695-2-12
|
|
热灯丝点火温度
|
|
|
IEC 60695-2-13
|
|
0.750 mm 13
|
875
|
°C
|
IEC 60695-2-13
|
|
1.50 mm
|
850
|
°C
|
IEC 60695-2-13
|