| 特性级别 | 热稳定性|||标准级|||圄静电|||高刚性||| |
| 牌号 | TG7S |
| 加工级别 | 注堕级|||脱模级|||吹膜级||| |
| 品名 | PA6 |
| 厂家(产地) | 德国巴斯夫 |
| 用途级别 | 汽车部件|||板材级|||照明灯具|||电动工具配件||| |
35%玻纤增强原装料PA6 TG7S
Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushion pan/frame to be made of an engineering plastic as opposed to metal. TG7S exhibits improved strength,stiffness and notched impact properties over Ultramid 8333G HI.
Applications
Include cushion seat pan/frame and other automotive seating applications, automotive fan, power tools and trimmer components.
Ultramid® TG7S 物性表
| 基本信息 | |
|---|---|
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.37 | g/cm3 | ISO 1183 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 | ISO 527-2 | ||
| 断裂, -40°C | 251 | MPa | ISO 527-2 |
| 断裂, 23°C | 170 | MPa | ISO 527-2 |
| 断裂, 80°C | 97.0 | MPa | ISO 527-2 |
| 断裂, 121°C | 77.0 | MPa | ISO 527-2 |
| 拉伸应变 (断裂, 23°C) | 3.3 | % | ISO 527-2 |
| 弯曲模量 (23°C) | 8400 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 (23°C) | 23 | kJ/m2 | ISO 179 |
| 悬壁梁缺口冲击强度 | ISO 180 | ||
| -40°C | 18 | kJ/m2 | ISO 180 |
| 23°C | 26 | kJ/m2 | ISO 180 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 (1.8 MPa, 未退火) | 203 | °C | ISO 75-2/A |
| 溶融温度（DSC） | 220 | °C | ISO 3146 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 80.0 | °C | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的*水分含量 | 0.080 | % | |
| 料筒后部温度 | 245 到 275 | °C | |
| 料筒中部温度 | 260 到 285 | °C | |
| 料筒前部温度 | 270 到 295 | °C | |
| 射嘴温度 | 270 到 295 | °C | |
| 加工（熔体）温度 | 270 到 295 | °C | |
| 模具温度 | 80.0 到 95.0 | °C | |
| 注塑压力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 |