全国咨询热线：13725716294
|
| 特性级别 | 阻燃级|||增强级|||标准级||| |
| 牌号 | CM1011G-45 |
| 加工级别 | |
| 品名 | PA6 |
| 厂家(产地) | 日本东丽 |
| 用途级别 | 填充级|||汽车部件|||电子电器部件||| |
45%玻璃纤维PA6 CM1011G-45
CM1011G-45
规格级别： 注塑
CM1011G-45 物性表
| 基本性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 吸水率 | ASTM D-570 | ||
| (23℃.24hr) | Dry|1.9%Water0.9|- | % | |
| (23℃) | Dry|1.9%Water5.3|- | % |
| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 比重 | Dry|1.9%Water1.50|- | ASTM D-792 |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 断裂伸长率 (-40℃) | Dry|1.9%Water4.5|4.5 | % | ASTM D-638 |
| 弯曲模量 (23℃) | Dry|1.9%Water12.0|7.1 | GPa | ASTM D-790 |
| IZOD缺口冲击强度 (-40℃) | Dry|1.9%Water125|145 | J/m | ASTM D-256 |
| 弯曲模量 (80℃) | Dry|1.9%Water6.2|4.4 | GPa | ASTM D-790 |
| 拉伸屈服强度 (23℃) | Dry|1.9%Water205|130 | MPa | ASTM D-638 |
| 弯曲模量 (-40℃) | Dry|1.9%Water14.0|12.5 | GPa | ASTM D-790 |
| 弯曲强度 (23℃) | Dry|1.9%Water290|180 | MPa | ASTM D-790 |
| 断裂伸长率 (23℃) | Dry|1.9%Water5.0|5.0 | % | ASTM D-638 |
| 拉伸屈服强度 (80℃) | Dry|1.9%Water120|85 | MPa | ASTM D-638 |
| IZOD无缺口冲击强度 (23℃) | Dry|1.9%Water100|120 | KJ/m | ASTM D-256 |
| 弯曲强度 (-40℃) | Dry|1.9%Water330|280 | MPa | ASTM D-790 |
| IZOD缺口冲击强度 (23℃) | Dry|1.9%Water155|195 | J/m | ASTM D-256 |
| 抗压强度 | ASTM D-695 | ||
| (-40℃) | Dry|1.9%Water260|220 | MPa | |
| (23℃) | Dry|1.9%Water190|120 | MPa | |
| (80℃) | Dry|1.9%Water100|70 | MPa | |
| 剪切强度 (23℃) | Dry|1.9%Water95|75 | MPa | ASTM D-732 |
| 断裂伸长率 (80℃) | Dry|1.9%Water8.0|8.0 | % | ASTM D-638 |
| 弯曲强度 (80℃) | Dry|1.9%Water160|110 | MPa | ASTM D-790 |
| 洛氏硬度 (23℃) | Dry|1.9%WaterR121,M95|- | R Scale | ASTM D-785 |
| IZOD无缺口冲击强度 (-40℃) | Dry|1.9%Water90|95 | KJ/m | ASTM D-256 |
| 拉伸屈服强度 (-40℃) | Dry|1.9%Water290|250 | MPa | ASTM D-638 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 热导率 | Dry|1.9%Water0.40|- | W/m℃ | |
| 线性热膨胀系数 | Dry|1.9%Water2-3|- | 10-5/℃ | ASTM D-696 |
| 比热 | Dry|1.9%Water1.4|- | J/p℃ | |
| 熔点 | Dry|1.9%Water225|- | ℃ | DSC |
| 热变形温度 | ASTM D-648 | ||
| (0.46MPa) | Dry|1.9%Water225|- | ℃ | |
| (1.86MPa) | Dry|1.9%Water215|- | ℃ |
| 其它性能 | 额定值 | 单位 |
|---|