特性级别 | 阻燃级|||高结晶(HCPP)||| |
牌号 | GP-1000FC |
品名 | PP |
厂家(产地) | 韩国LG |
用途级别 | 板材级|||电线电缆级|||电动工具配件||| |
LG PP GP-1000FC
LG Chemical GP1000FC PP
Polymer,Thermoplastic,Polypropylene (PP),Polypropylene, Flame Retardant
LG Chemical
产品说明:
Description: Injection Molding, FR PP, General Purpose, Flame Retardant
Application: Electrical & Electronic, Automotive Parts
CAS: 9003-07-0 and 1309-64-4
Information provided by LG Chemical
GP1000FC PP 物性表
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
比重 | 1.00 g/cc | 1.00 g/cc | ASTM D792 |
处理 | 0.010 | 0.010 | Injection Molding |
线性成型收缩率,Flow | 0.016 - 0.018 cm/cm @Thickness 3.20 mm | 0.016 - 0.018 in/in @Thickness 0.126 in | ASTM D955 |
熔体流动速率 | 14 g/10 min @Load 2.16 kg, Temperature 230 °C | 14 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
抗张强度(屈服) | 32.4 MPa @Thickness 3.20 mm | 4690 psi @Thickness 0.126 in | 50mm/min; ASTM D638 |
伸长率 (断裂) | 70 % @Thickness 3.20 mm | 70 % @Thickness 0.126 in | 50mm/min; ASTM D638 |
弯曲强度 | 38.2 MPa @Thickness 6.40 mm | 5550 psi @Thickness 0.252 in | 10mm/min; ASTM D790 |
弯曲模量 | 1.77 GPa @Thickness 6.40 mm | 256 ksi @Thickness 0.252 in | 10mm/min; ASTM D790 |
悬壁梁缺口冲击强度 | 0.490 J/cm @Thickness 6.40 mm, Temperature 23.0 °C | 0.918 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F | ASTM D256 |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
耐电弧性 | 60 - 120 sec | 60 - 120 sec | ASTM D495 |
热丝引燃 (HWI) | 7.0 - 15 sec @Thickness >=0.750 mm | 7.0 - 15 sec @Thickness >=0.0295 in | |
15 - 30 sec @Thickness >=1.50 mm | 15 - 30 sec @Thickness >=0.0591 in | ||
30 - 60 sec @Thickness >=3.00 mm | 30 - 60 sec @Thickness >=0.118 in | ||
高电弧燃烧指数(HAI) | >= 120 arcs @Thickness 0.750 mm | >= 120 arcs @Thickness 0.0295 in | |
>= 120 arcs @Thickness 1.50 mm | >= 120 arcs @Thickness 0.0591 in | ||
>= 120 arcs @Thickness 3.00 mm | >= 120 arcs @Thickness 0.118 in |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
载荷下热变形温度(0.46 MPa) | 120 °C @Thickness 3.20 mm | 248 °F @Thickness 0.126 in | Unannealed; ASTM D648 |
UL RTI | 120 °C @Thickness >=0.750 mm | 248 °F @Thickness >=0.0295 in | |
120 °C @Thickness >=1.50 mm | 248 °F @Thickness >=0.0591 in | ||
120 °C @Thickness >=3.00 mm | 248 °F @Thickness >=0.118 in | ||
UL RTI,机械冲击 | 120 °C @Thickness >=0.750 mm | 248 °F @Thickness >=0.0295 in | |
120 °C @Thickness >=1.50 mm | 248 °F @Thickness >=0.0591 in | ||
120 °C @Thickness >=3.00 mm | 248 °F @Thickness >=0.118 in |